Highly active sites of low spin FeⅡN4species:The identification and the ORR performance

Over recent years,catalytic materials of Fe-N-C species have been recognized being active for oxygen reduction reaction(ORR).However,the identification of active site remains challenging as it generally involves a pyrolysis process and mixed components being obtained.Herein Fe₃C/C and Fe₂N/C samples were synthesized by temperature programmed reduction of Fe precursors in 15%CH₄/H₂and pure NH₃,respectively.By acid leaching of Fe₂N/C sample,only single sites of FeN₄species were presented,providing an ideal model for identification of catalytic functions of the single sites of FeN₄in ORR.A correlation was conducted between the concentration of Fe^ⅡN₄in low spin state by Mossbauer spectra and the kinetic current density at 0.8 V in alkaline media,and such a structure-performance correlation assures the catalytic roles of low spin Fe^ⅡN₄ species as highly active sites for the ORR.     

钒掺杂二氧化钛光催化活性研究

二氧化钛凭借优异的光催化性能,越来越受到人们的广泛关注和重视。以钛酸四丁酯为原料,利用水解-水热-干燥/煅烧工艺制备得到未掺杂TiO₂光催化剂和掺钒TiO₂光催化剂,利用其对甲基橙溶液的降解率做了比较分析。结果表明,以钛酸四丁酯为原料,采用溶胶-凝胶法制备钒掺杂TiO₂光催化剂是可行的。制备V/TiO₂产品的最佳工艺条件：钒钛质量比为6∶100、水热温度为160 ℃、水热时间为12 h,120 ℃下干燥14 h。紫外光照射条件下,甲基橙光催化降解效率达到99.10%,降解时间小于45 min。     

多晶硅锭中硬质点分析及控制研究

以多晶硅锭中硬质点为研究对象,通过实验研究和数值模拟的方法,对多晶硅锭中硬质点进行形貌和成分分析,并提出改善控制方法。研究结果表明硅锭中部的硬质点较细小,主要由SiC组成;硅锭头部的硬质点较粗大,主要由SiC和Si3N4组成,还有少量O的存在。进一步研究发现多晶硅定向凝固铸锭炉的热场结构对于多晶硅锭硬质点形成有直接影响,通过改进热场结构,优化晶体生长界面,显著减少了铸锭中硬质点的数量。     

改性剂用量对紫炭黑填充天然橡胶/顺丁橡胶并用胶性能的影响

研究改性剂（间苯二酚/六次亚甲基四胺共混物）用量对紫炭黑填充天然橡胶/顺丁橡胶并用胶性能的影响。结果表明：随着改性剂用量增大，胶料的硬度和定伸应力提高，拉伸强度、撕裂强度先下降后提高，阿克隆磨耗量先增大后减小；当改性剂/紫炭黑用量比为4%时，胶料的物理性能较好。添加改性剂可提高紫炭黑对胶料的补强作用，并在一定程度上改善胶料的热稳定性。